| Properties |
Description |
| Adhesive |
1-mil, super clear, permanent acrylic pressure sensitive adhesive |
| Carrier |
1 mil clear polyester |
| Release Liner |
2 mil, 40# polycoated Kraft paper |
| Peel Adhesion |
(PSTC 1, modified for 72 hour dwell time): Stainless steel = 41 oz./in.; Acrylic = 2 oz./in.; Glass = 39 oz./in. |
| Shear Strength |
(PSTC 7, 1 hour dwell, 1 sq in, 4 lb load): 100+ hours no failure |
| Tack |
(ASTM D2979-88): 350 gm/sq. cm |
| Laminator Compatibility |
It's recommended that your laminator be equipped with a release liner take-up reel. All LexJet laminates are provided on 3" standard cores. |
| Laminator Settings |
Apply 80-100 psi and use 2-3 feet per minute for dwell time. Between 90° to 100° F heat is recommended, to help the adhesive flow will produce a more consistent adhesion to the print. All substrates should be tested for your specific application prior to final job production. |
| Using a Sled |
It is strongly recommended that you use a rigid sled (1/8" or thicker) such as polycarbonate, acrylic, masonite or aluminum. This will ensure consistent pressure across the web. Apply a release liner to your sled to prevent adhesive build-up. Use strong tape, such as packaging tape, to attach the entire width of the leading edge of the graphic to the sled. |
| Adhesive Cure Time |
After applying the laminate, allow curing for a minimum of 2 hours before cutting or trimming. Maximum bond strength is reached in 24 hours. |
| Service Temp. Range |
-20° F to 257° F (-29° to 125° C ) THIS IS NOT A LAMINATOR SETTING. |
| Ideal Storage Conditions |
70° F (21° C), 50% R.H. (a controlled environment is recommended); store vertically in original packaging. |
| Shelf Life |
1 year from the LexJet ship date when stored in proper conditions. |
| Application Recommendations |
This product can be applied using wet or dry method |