| Properties |
Description |
| Material |
3.2 Mil luster flexible calendered PVC film |
| Adhesive |
A 1 Mil ultra clear, UV resistant, thermo set, permanent acrylic pressure sensitive adhesive. |
| Release Liner |
2 Mil 40# polycoated Kraft paper. |
| Gloss Level at 60° |
35 |
| Peel Adhesion |
(Test method PSTC-1): Stainless Steel= 45-70 oz./in.; Acrylic= 55-85 oz./in.; Polypropylene= 20-45 oz./in. |
| Shear Strength |
PSTC 7, 1 hour dwell time, 1 sq. in 4 lb. load,: 25+ hours |
| UVA Light Protection |
90-95% |
| Inkjet Media Preparation |
Printer manufacturers recommend that you allow your print to dry for a minimum of 24 hours before lamination. In areas with high humidity dry times can be longer. |
| Laminator Compatibility |
It's recommended that your laminator be equipped with a release liner take-up reel. All LexJet laminates are provided on 3" standard cores. |
| Laminator Settings |
NO HEAT IS REQUIRED. Apply 40-80 psi and use 2-5 feet per minute for dwell time, depending on the application. The top and bottom web tension should be minimal so memory will not be a factor. |
| Adhesive Cure Time |
After applying the laminate, allow curing for a minimum of 2 hours before cutting or trimming. Maximum bond strength is reached in 24 hours. |
| Min. Application Temp. |
50° F (10° C) |
| Ideal Storage Conditions |
70° F (21° C), 50% R.H. (a controlled environment is recommended); store vertically in original packaging. |
| Shelf Life |
1 year from the LexJet ship date when stored in proper conditions. |